TECHNICAL DATA SHEETS

Yicaiplas Polymer Solutions | Document Rev. 2026-05

Shenzhen Yicaihongxiang New Materials

ISO 9001:2015 Certified

Color Masterbatch

Grade: YC-CM

TDS-YC-CM

Issue: 2026-05-06

1. DESCRIPTION

High-concentration pigment dispersion in polymer carrier for coloring thermoplastics. Provides consistent color reproduction, excellent dispersion, and minimal effect on base polymer properties.

2. KEY FEATURES

  • •Pigment concentration: 15-50%
  • •Excellent dispersion, no agglomeration
  • •Good thermal stability up to 280°C
  • •Low migration, high light fastness
  • •Compatible with PE, PP, ABS, PA, PC

3. TYPICAL APPLICATIONS

  • Injection molding (automotive parts, household appliances)
  • Extrusion (pipes, profiles, sheets)
  • Blow molding (bottles, containers)
  • Film production (packaging, agricultural)

4. TECHNICAL PROPERTIES

Carrier ResinPE / PP / ABS / PA / PC
Pigment Content15-50%
Recommended Dosage1-4%
Melt Temperature160-220°C
Density1.2-1.8 g/cm³
Light Fastness7-8 (ISO 105-B02)
Migration Resistance4-5 (ISO 105-X12)
Thermal Stability≥280°C (10 min)

5. PROCESSING PARAMETERS

Processing MethodInjection, extrusion, blow molding
Melt Temp Range160-240°C
Screw Speed50-150 rpm
L/D Ratio≥20:1
Drying RequiredRecommended 2-4h @ 80°C

6. STORAGE & HANDLING

Store in cool, dry place away from direct sunlight. Keep packaging sealed when not in use. Shelf life: 24 months from production date when stored properly.

7. SAFETY NOTICE

Refer to SDS for detailed safety information. Use appropriate PPE during processing.

8. DISCLAIMER

Data provided for general guidance. Actual properties may vary with processing conditions. User testing required for application suitability. Specifications subject to change without notice.

Flame Retardant Masterbatch

Grade: YC-FR

TDS-YC-FR

Issue: 2026-05-06

1. DESCRIPTION

Halogen-free flame retardant concentrate for achieving UL94 V-0 rating in thermoplastics. Suitable for electrical and electronic applications requiring fire safety compliance.

2. KEY FEATURES

  • •Halogen-free formulation
  • •UL94 V-0 / V-1 / V-2 achievable
  • •High LOI: 28-35%
  • •Good mechanical property retention
  • •Low smoke emission

3. TYPICAL APPLICATIONS

  • Wire and cable insulation
  • Electrical connectors and housings
  • Construction materials (conduit, panels)
  • Automotive interior components
  • Electronic device enclosures

4. TECHNICAL PROPERTIES

Carrier ResinPE / PP / ABS / PA
Active Agent Content30-60%
Recommended Dosage5-15%
Melt Temperature170-230°C
Density1.5-2.2 g/cm³
UL94 RatingV-0 / V-1 / V-2
LOI28-35%
Halogen Content<900 ppm

5. PROCESSING PARAMETERS

Processing MethodInjection, extrusion
Melt Temp Range170-250°C
Screw Speed50-120 rpm
Mold Temp20-60°C
NoteAvoid excessive shear

6. STORAGE & HANDLING

Store in cool, dry place. Protect from moisture. Keep away from oxidizing agents. Shelf life: 18 months from production date.

7. SAFETY NOTICE

Refer to SDS for detailed safety information. Use appropriate PPE during processing.

8. DISCLAIMER

Data provided for general guidance. Actual properties may vary with processing conditions. User testing required for application suitability. Specifications subject to change without notice.

Anti-UV Masterbatch

Grade: YC-UV

TDS-YC-UV

Issue: 2026-05-06

1. DESCRIPTION

UV stabilizer concentrate for outdoor applications. Provides long-term weather resistance, preventing color fading and mechanical property degradation from UV exposure.

2. KEY FEATURES

  • •UV resistance: 1000-2000h (QUV)
  • •Hindered amine light stabilizers (HALS)
  • •UV absorbers (UVA) included
  • •Synergistic effect with antioxidants
  • •Suitable for outdoor applications

3. TYPICAL APPLICATIONS

  • Automotive exterior parts
  • Outdoor furniture and equipment
  • Agricultural film
  • Building profiles and siding
  • Marine applications

4. TECHNICAL PROPERTIES

Carrier ResinPE / PP / ABS / ASA
Active Agent Content10-30%
Recommended Dosage2-5%
Melt Temperature160-220°C
Density1.1-1.5 g/cm³
UV Resistance1000-2000h (QUV)
Property Retention>80% tensile after aging
Color StabilityΔE < 3 after 1000h

5. PROCESSING PARAMETERS

Processing MethodInjection, extrusion, blow molding
Melt Temp Range160-230°C
Screw Speed50-150 rpm
NoteCombine with antioxidant for best results

6. STORAGE & HANDLING

Store in cool, dry place away from UV light. Keep packaging sealed. Shelf life: 24 months from production date.

7. SAFETY NOTICE

Refer to SDS for detailed safety information. Use appropriate PPE during processing.

8. DISCLAIMER

Data provided for general guidance. Actual properties may vary with processing conditions. User testing required for application suitability. Specifications subject to change without notice.

Anti-Bacterial Masterbatch

Grade: YC-AB

TDS-YC-AB

Issue: 2026-05-06

1. DESCRIPTION

Antimicrobial concentrate with silver/zinc ion technology. Provides long-lasting bacterial inhibition for hygiene-sensitive applications. Compliant with ISO 22196.

2. KEY FEATURES

  • •Bacterial reduction >99.9% (ISO 22196)
  • •Silver/Zinc ion technology
  • •Long-lasting efficacy
  • •Safe for food contact applications
  • •Durable through multiple wash cycles

3. TYPICAL APPLICATIONS

  • Medical devices and equipment
  • Food packaging and containers
  • Sanitary products
  • Public facility surfaces
  • Kitchenware and household items

4. TECHNICAL PROPERTIES

Carrier ResinPE / PP / ABS
Active AgentAg/Zn ions (1-5%)
Recommended Dosage1-3%
Melt Temperature160-220°C
Density1.2-1.6 g/cm³
Bacterial Reduction>99.9% (ISO 22196)
Durability10+ wash cycles
Food ContactFDA compliant

5. PROCESSING PARAMETERS

Processing MethodInjection, extrusion, blow molding
Melt Temp Range160-230°C
Screw Speed50-120 rpm
NoteAvoid temperatures >250°C

6. STORAGE & HANDLING

Store in cool, dry place. Avoid contamination. Keep packaging sealed. Shelf life: 24 months from production date.

7. SAFETY NOTICE

Refer to SDS for detailed safety information. Use appropriate PPE during processing.

8. DISCLAIMER

Data provided for general guidance. Actual properties may vary with processing conditions. User testing required for application suitability. Specifications subject to change without notice.

Modified Plastics - PP GF30

Grade: YC-MP-PP30

TDS-YC-MP-PP30

Issue: 2026-05-06

1. DESCRIPTION

30% glass fiber reinforced polypropylene compound. High stiffness, dimensional stability, and heat resistance for structural applications. Automotive grade with OEM approvals.

2. KEY FEATURES

  • •30% glass fiber reinforcement
  • •High stiffness: Flexural modulus 6000 MPa
  • •Heat deflection temp: 155°C @ 0.45 MPa
  • •Low shrinkage: 0.2-0.4%
  • •Automotive OEM approved

3. TYPICAL APPLICATIONS

  • Automotive: Instrument panels, door modules
  • Appliance: Washing machine tubs, dryer drums
  • Industrial: Pump housings, valve bodies
  • Electronics: Connector housings
  • Furniture: Structural frames

4. TECHNICAL PROPERTIES

Base PolymerPolypropylene (PP) homopolymer
Glass Fiber Content30 ± 2%
Density1.12 g/cm³ (ISO 1183)
Tensile Strength85 MPa (ISO 527)
Tensile Modulus5500 MPa (ISO 527)
Flexural Strength120 MPa (ISO 178)
Flexural Modulus6000 MPa (ISO 178)
Impact Strength (Notched Izod)10 kJ/m² @ 23°C (ISO 180)
HDT (0.45 MPa)155°C (ISO 75-2)
HDT (1.8 MPa)145°C (ISO 75-2)
Vicat Softening Point162°C (ISO 306)
Melt Flow Rate8 g/10min @ 230°C/2.16kg (ISO 1133)
Shrinkage (Flow)0.2-0.3%
Shrinkage (Transverse)0.3-0.4%

5. PROCESSING PARAMETERS

Processing MethodInjection molding
Melt Temperature200-230°C
Mold Temperature40-60°C
Injection Pressure80-120 MPa
Injection SpeedMedium to high
Holding Pressure40-60 MPa
Screw Speed40-80 rpm
Drying RequiredRecommended 2-4h @ 80°C if moisture >0.1%

6. STORAGE & HANDLING

Store in dry conditions at 15-30°C, relative humidity <70%. Protect from direct sunlight. Keep bags sealed. Shelf life: 24 months from production date.

7. SAFETY NOTICE

Refer to SDS for detailed safety information. Use appropriate PPE during processing.

8. DISCLAIMER

Data provided for general guidance. Actual properties may vary with processing conditions. User testing required for application suitability. Specifications subject to change without notice.

Modified Plastics - PA6 GF30

Grade: YC-MP-PA30

TDS-YC-MP-PA30

Issue: 2026-05-06

1. DESCRIPTION

30% glass fiber reinforced nylon 6 compound. Excellent mechanical strength, wear resistance, and chemical resistance. Heat stabilized for under-hood automotive applications.

2. KEY FEATURES

  • •30% glass fiber reinforcement
  • •High tensile strength: 170 MPa
  • •Excellent fatigue resistance
  • •Heat stabilized for continuous use @ 120°C
  • •Good chemical resistance to oils/fuels

3. TYPICAL APPLICATIONS

  • Automotive: Engine covers, intake manifolds, gears
  • Industrial: Gear wheels, bearings, bushings
  • Electrical: Connectors, terminal blocks
  • Consumer: Power tool housings
  • Sports: Ski bindings, bicycle components

4. TECHNICAL PROPERTIES

Base PolymerNylon 6 (PA6) - Heat stabilized
Glass Fiber Content30 ± 2%
Density1.36 g/cm³ (ISO 1183)
Tensile Strength170 MPa (ISO 527)
Tensile Modulus9000 MPa (ISO 527)
Elongation at Break3.5% (ISO 527)
Flexural Strength240 MPa (ISO 178)
Flexural Modulus8500 MPa (ISO 178)
Impact Strength (Charpy Notched)12 kJ/m² @ 23°C (ISO 179)
HDT (1.8 MPa)200°C (ISO 75-2)
Vicat Softening Point215°C (ISO 306)
Melt Flow Rate15 g/10min @ 275°C/5kg (ISO 1133)
Water Absorption (23°C, 50%RH)1.2% (ISO 62)
Water Absorption (Saturation)6.5% (ISO 62)

5. PROCESSING PARAMETERS

Processing MethodInjection molding
Melt Temperature260-280°C
Mold Temperature80-100°C
Injection Pressure100-150 MPa
Injection SpeedHigh
Screw Speed50-100 rpm
Drying RequiredRequired 4-6h @ 80°C (moisture <0.15%)
NoteMoisture causes surface defects and property degradation

6. STORAGE & HANDLING

Store in dry conditions. Moisture-sensitive - keep packaging sealed. Recommended storage: 15-25°C, RH <60%. Shelf life: 12 months in original packaging. Dry before use if opened.

7. SAFETY NOTICE

Refer to SDS for detailed safety information. Use appropriate PPE during processing.

8. DISCLAIMER

Data provided for general guidance. Actual properties may vary with processing conditions. User testing required for application suitability. Specifications subject to change without notice.

Modified Plastics - ABS FR

Grade: YC-MP-AFR

TDS-YC-MP-AFR

Issue: 2026-05-06

1. DESCRIPTION

Flame retardant ABS compound achieving UL94 V-0 rating. Halogen-free formulation for electrical and electronic enclosures. Good impact strength and surface finish.

2. KEY FEATURES

  • •UL94 V-0 @ 1.5mm thickness
  • •Halogen-free formulation
  • •LOI: 29%
  • •Good surface gloss
  • •RoHS / REACH compliant

3. TYPICAL APPLICATIONS

  • Electrical: Switch boxes, circuit breaker housings
  • Electronics: Monitor housings, printer cases
  • Appliance: TV backs, power supply cases
  • Automotive: Electrical connectors, relay housings
  • Industrial: Control panel enclosures

4. TECHNICAL PROPERTIES

Base PolymerABS (Acrylonitrile Butadiene Styrene)
Flame Retardant SystemPhosphorus-based, halogen-free
Density1.18 g/cm³ (ISO 1183)
Tensile Strength42 MPa (ISO 527)
Tensile Modulus2200 MPa (ISO 527)
Elongation at Break15% (ISO 527)
Flexural Strength65 MPa (ISO 178)
Flexural Modulus2100 MPa (ISO 178)
Impact Strength (Izod Notched)15 kJ/m² @ 23°C (ISO 180)
HDT (1.8 MPa)85°C (ISO 75-2)
Vicat Softening Point95°C (ISO 306)
Melt Flow Rate18 g/10min @ 220°C/10kg (ISO 1133)
UL94 RatingV-0 @ 1.5mm
LOI29% (ISO 4589-2)

5. PROCESSING PARAMETERS

Processing MethodInjection molding, extrusion
Melt Temperature200-240°C
Mold Temperature50-70°C
Injection Pressure70-110 MPa
Injection SpeedMedium
Screw Speed40-80 rpm
Drying RequiredRequired 2-4h @ 80°C (moisture <0.1%)

6. STORAGE & HANDLING

Store in dry, cool place. Moisture-sensitive. Keep packaging sealed. Shelf life: 24 months from production date when stored properly.

7. SAFETY NOTICE

Refer to SDS for detailed safety information. Use appropriate PPE during processing.

8. DISCLAIMER

Data provided for general guidance. Actual properties may vary with processing conditions. User testing required for application suitability. Specifications subject to change without notice.

ASA Alloy Material

Grade: YC-ASA

TDS-YC-ASA

Issue: 2026-05-06

1. DESCRIPTION

Acrylonitrile Styrene Acrylate alloy with exceptional weather resistance. Maintains color and mechanical properties after long-term outdoor exposure. Ideal for automotive and building applications.

2. KEY FEATURES

  • •UV resistance: 2000-4000h (QUV)
  • •Excellent color retention
  • •Good impact strength
  • •No painting required
  • •Automotive exterior grade

3. TYPICAL APPLICATIONS

  • Automotive exterior trim
  • Building profiles and siding
  • Outdoor enclosures
  • Marine components
  • Garden equipment

4. TECHNICAL PROPERTIES

Base MaterialASA / ASA+PMMA
UV Resistance2000-4000h (QUV)
Melt Temperature200-240°C
Density1.05-1.15 g/cm³
Tensile Strength35-50 MPa
Impact Strength10-25 kJ/m² (Notched Izod)
Color RetentionΔE < 3 after 2000h UV
Gloss Retention>80% after 2000h

5. PROCESSING PARAMETERS

Processing MethodInjection, extrusion
Melt Temp Range200-260°C
Mold Temp40-80°C
Drying RequiredRequired 3-4h @ 80-90°C
Screw Speed60-120 rpm

6. STORAGE & HANDLING

Store in dry, cool place. Protect from moisture. Shelf life: 24 months from production date when stored properly.

7. SAFETY NOTICE

Refer to SDS for detailed safety information. Use appropriate PPE during processing.

8. DISCLAIMER

Data provided for general guidance. Actual properties may vary with processing conditions. User testing required for application suitability. Specifications subject to change without notice.

ASA Colored Film

Grade: YC-ASA-F

TDS-YC-ASA-F

Issue: 2026-05-06

1. DESCRIPTION

Pre-colored ASA film for surface lamination applications. Provides UV-resistant, color-stable surface finish without painting. Suitable for automotive trim and architectural cladding.

2. KEY FEATURES

  • •Thickness: 50-200 μm
  • •Excellent UV resistance
  • •Color matching available
  • •Good adhesion to substrates
  • •No painting required

3. TYPICAL APPLICATIONS

  • Automotive trim lamination
  • Architectural cladding
  • Window and door profiles
  • Furniture surface finish
  • Signage and displays

4. TECHNICAL PROPERTIES

Thickness50-200 μm
Width500-1500 mm
UV Resistance2000-4000h (QUV)
Gloss10-90 GU (60°)
Elongation at Break>100%
Tensile Strength25-40 MPa
Color StabilityΔE < 3 after 2000h UV
Adhesion>1.5 N/mm

5. PROCESSING PARAMETERS

Application MethodThermal lamination, adhesive bonding
Lamination Temp120-180°C
Pressure0.3-0.8 MPa
SubstratePVC, ABS, PP, Metal
Storage Temp15-25°C

6. STORAGE & HANDLING

Store in cool, dry place. Roll storage: horizontal, avoid pressure marks. Shelf life: 12 months from production date.

7. SAFETY NOTICE

Refer to SDS for detailed safety information. Use appropriate PPE during processing.

8. DISCLAIMER

Data provided for general guidance. Actual properties may vary with processing conditions. User testing required for application suitability. Specifications subject to change without notice.

Biodegradable Plastics

Grade: YC-BIO

TDS-YC-BIO

Issue: 2026-05-06

1. DESCRIPTION

Compostable polymer compounds based on PLA/PBAT/PBS blends. Certified to EN 13432 and ASTM D6400 standards. Suitable for disposable packaging and agricultural applications.

2. KEY FEATURES

  • •EN 13432 / ASTM D6400 certified
  • •Industrial compostable (3-6 months)
  • •Food contact approved
  • •Renewable content available
  • •Customizable degradation rate

3. TYPICAL APPLICATIONS

  • Disposable food packaging
  • Shopping bags and produce bags
  • Agricultural mulch film
  • Compostable cutlery
  • Waste collection bags

4. TECHNICAL PROPERTIES

Base MaterialPLA / PBAT / PBS / Starch
BiodegradabilityEN 13432 / ASTM D6400
Melt Temperature120-180°C
Density1.2-1.4 g/cm³
Tensile Strength20-50 MPa
Elongation at Break100-600%
Compost Time3-6 months (industrial)
Bio Content20-100%

5. PROCESSING PARAMETERS

Processing MethodInjection, extrusion, blow molding
Melt Temp Range120-180°C
Screw Speed40-100 rpm
Drying RequiredRequired 4-6h @ 40-60°C
NoteAvoid temperatures >200°C

6. STORAGE & HANDLING

Store in cool, dry place. Moisture-sensitive. Keep packaging sealed. Shelf life: 12 months from production date. Use within 3 months after opening.

7. SAFETY NOTICE

Refer to SDS for detailed safety information. Use appropriate PPE during processing.

8. DISCLAIMER

Data provided for general guidance. Actual properties may vary with processing conditions. User testing required for application suitability. Specifications subject to change without notice.

Engineering Contact: [email protected] | Technical Support: +86-755-XXXX | www.yicaiplas.com

💬
Request a Quote